OLV6688 High Grade Insulating Glass Silicone Sealant

This product is a two-component, neutral room-temperature-curing silicone sealant.

Product Detail

The insulating glass is bonded and sealed in two layers.

1. High strength, good bonding performance, and low air permeability;

2. Excellent weather resistance, aging resistance;

3. Exhibits outstanding high and low temperature resistance;

4. Excellent adhesion to most building materials;

5. Component A of this product is white, component B is black, and the mixture appears black.

1. It should not be used as a structural sealant;

2. Not suitable for the surface of materials that will seep grease, plasticizer or solvent;

3. Not suitable for frosted or wet surfaces and places soaked in water or wet all the year round;

4. The surface temperature of the substrate should not be below 4°C or above 40°C during application.

(180+18)L/(18+2)L

(190+19)L/(19+2)L

A component: white, B component: black

Store in a dry, ventilated, and cool place in the original sealed condition, with a maximum storage temperature of 27°C.

The shelf life is 12 months.

OLV6688 High Grade Insulating Glass Silicone Sealant
Performance		Standard	Measured Value	Testing Method
Test at 50±5% RH and temperature 23±20°C:
Density (g/cm³)		--	A: 1.50 B: 1.02	GB/T 13477
Skin-Free Time (min)		≤180	45	GB/T 13477
Extrusion (ml/min)		/	/	GB/T 13477
Slumpability (mm) vertical		≤3	0	GB/T 13477
Slumpability (mm) horizontal		not change shape	not change shape	GB/T 13477
Period of application(min)		≥20	35	GB/16776-2005
As Cured -After 21 days at 50±5% RH and temperature 23±2°C:
Hardness (Shore A)		30~60	37	GB/T 531
Tensile Strength under Standard Conditions (Mpa)		≥0.60	0.82	GB/T 13477
Elongation at maximum tensile(%)		≥100	214	GB/T 13477
Storage	12 Months